P265GH Pipe Bend

Manufacturing Sizes :

• Seamless : 1/2″ To 32″
• Welded : 12″ To 60″
• Buttweld : 1/2″ To 24″

Common Thickness :

• SCH 10 To SCH 160 XXS

Forming Method :

• Cold formed
• Hot formed

Ends Types :

• Butt welding
• Bevelled
• Plain Bevel

Test Certificates :

• Raw Materials Certificate
• MTR Report
• Third Party Inspection Repor
• EN 10204/3.1B,

Packaging :

• Carton Box
• Wooden Cases
• Wooden Pallet

Installations :

• Refrigerant fittings
• Pressure vessels systems
• Nuclear energy sector
• Mechanical systems
• Petrochemical plants

ISO Standard :

• ISO 5251

Melting Point :

• 1480°C

Logistics :

• By Air
• By Sea
• Oman = 5 to 6 days
• Saudi Arabia = 7 to 8 day
• Qatar = 7 day
• UAE = 6 to 7 day
• Bahrain = 9 to 10 days

Density :

• 7.8 mm²/s

Hardness :

• 102 HB

Radius Of Bend :

• 1.5D & 2.5D
• 3D & 5D
• 6D & 8D
• 10D & 22D

Angle Of Bend :

• 15 Deg & 20 Deg
• 45 Deg & 60 Deg
• 90 Deg & 120 Deg
• 135 Deg & 180 Deg

Heat Treatment :

• 880 to 940 °C

Weight Calculation :

• θ = Angle
• D = Diameter
• L = Weight
• T = Thickness
• R = Radius

Available Documentation :

• Heat treatment charts
• Welding procedure specification
• Raw material test reports

ASME Standard :

• ASME B16.9
• ASME B16.28

Advantages :

• Easily cleaned
• High strength
• Easy to weld

Types Of Coating :

• Anti rust light oiling
• FBE coated
• Hot-dip galvanizing
• Back painting
• PE coating
• Varnished

Method :

• Welded
• Seamless
• Buttweld

Welding Method :

• GMAW welding
• TIG welding
• FCAW welding
• SMAW welding

Testing :

• Eddy current test
• Corrosion testing
• Ultrasonic test
• PMI test
• Thickness gauge
• Hyrdrostatic test
• Mechanical testing
• HIC test
• Magnetic Particle Examination

Method Of Bending :

• Roll bending
• Press bending
• Heating bending
• Liquid filling bending
• Tensile bending
• Compression bending

Process :

• Pressing
• Forging
• Bending
• Squeezing
• Machining

Number :

• 1.0425

Connection :

• Welding

Manganese [Mn] :

• max 1.40%

Silicon [Si] :

• max 0.40%

Phosphorus [P] :

• 0.025%

Sulfur [S] :

• 0.01%

Carbon [C] :

• max 0.20%

Copper (Cu) :

• max 0.30%

Chromium (Cr) :

• max 0.30%

Nickel (Ni) :

• max 0.30%

Vanadium (V) :

• max 0.02%

Titanium (Ti) :

• max 0.04%

Aluminum (AI) :

• min 0.020%

Tensile Strength (Rm)

• 410-570 MPa

Yield point in MPa

• –

Elongation A5 min

• 23%