P235GH Pipe Bend

Available Sizes :

• Welded : 12″ To 60″
• Buttweld : 1/2″ To 24″
• Seamless : 1/2″ To 32″

Schedule :

• SCH 10 To SCH 160 XXS

Forming :

• Hot formed
• Cold formed

Ends :

• Bevelled
• Plain Bevel
• Butt welding

Test Certificates :

• MTR Report
• Third Party Inspection Repor
• EN 10204/3.1B,
• Raw Materials Certificate

Packaging Types :

• Wooden Cases
• Wooden Pallet
• Carton Box

Used For :

• Nuclear energy sector
• Mechanical systems
• Petrochemical plants
• Refrigerant fittings
• Pressure vessels systems

ISO Standard :

• ISO 5251

Melting Completion (Liquidus) :

• 2660°F

Logistics :

• By Sea
• By Air
• Qatar = 7 day
• UAE = 6 to 7 day
• Bahrain = 9 to 10 days
• Oman = 5 to 6 days
• Saudi Arabia = 7 to 8 day

Density :

• 7.85 g/cm³

Hardness :

• 120 HB

Bend Radius Types :

• 1.5D & 2.5D
• 3D & 5D
• 6D & 8D
• 10D & 22D

Bend Angle Types :

• 15 Deg & 20 Deg
• 45 Deg & 60 Deg
• 90 Deg & 120 Deg
• 135 Deg & 180 Deg

Heat Treatment :

• +N = Normalized
• NT = Normalized and tempered

Weight Calculation :

• L = Weight
• T = Thickness
• R = Radius
• θ = Angle
• D = Diameter

Documentation :

• Welding procedure specification
• Raw material test reports
• Heat treatment charts

American Standard :

• ASME B16.9
• ASME B16.28

Advantages :

• High strength
• Easy to weld
• Easily cleaned

Different Coating :

• Hot-dip galvanizing
• Back painting
• PE coating
• Varnished
• Anti rust light oiling
• FBE coated

Method :

• Seamless
• Buttweld
• Welded

Welding :

• FCAW welding
• SMAW welding
• GMAW welding
• TIG welding

Testing Requirements :

• PMI test
• Thickness gauge
• Hyrdrostatic test
• Mechanical testing
• HIC test
• Magnetic Particle Examination
• Eddy current test
• Corrosion testing
• Ultrasonic test

Technique Of Bending :

• Heating bending
• Liquid filling bending
• Tensile bending
• Compression bending
• Roll bending
• Press bending

Process :

• Bending
• Squeezing
• Machining
• Pressing
• Forging

Number :

• 1.0345

Connection Method :

• Welding

Manganese [Mn] :

• max 1.20%

Silicon [Si] :

• max 0.35%

Phosphorus [P] :

• 0.025%

Sulfur [S] :

• 0.01%

Carbon [C] :

• max 0.16%

Copper (Cu) :

• max 0.30%

Chromium (Cr) :

• max 0.30%

Nickel (Ni) :

• max 0.30%

Vanadium (V) :

• max 0.02%

Titanium (Ti) :

• max 0.04%

Aluminum (AI) :

• min 0.020%

Tensile Strength (min)

• 360-500 MPa

Elongation A5 min

• 25%