P235GH Flange

P235GH flange

P235GH TC1 blind flanges

P235GH TC1 blind flanges

Werkstoff P235GH TC1 weld neck flanges

Werkstoff P235GH TC1 weld neck flanges

Steel Grade P235GH slip on flanges

Steel Grade P235GH slip on flanges

 

 

Specifications of EN 10216-2 P235GH pipe flange as per ASME B16.5

P235GH flange specifications

 

 

 

 

Buy most selling types of P235GH EN 10217-2 forged flanges for petrochemical plants

Types of EN 10216-2 P235GH pipe flange

EN 10216-2 P235GH socket weld flange

EN 10216-2 P235GH socket weld flange

P235GH EN 10217-2 lap joint flange

P235GH EN 10217-2 lap joint flange

P235GH TC1 plate flanges

P235GH TC1 plate flanges

Werkstoff P235GH TC1 long neck flanges

Werkstoff P235GH TC1 long neck flanges

Steel Grade P235GH threaded flange

Steel Grade P235GH threaded flange

Carbon steel P235GH orifice flange

Carbon steel P235GH orifice flange

Pressure vessel P235GH spectacle blind flanges

Pressure vessel P235GH spectacle blind flanges

P235GH (1.0345) reducing flange

P235GH (1.0345) reducing flange

EN P235GH grade 10216-2 RTJ flanges

EN P235GH grade 10216-2 RTJ flanges

 

Leading P235GH TC1 blind flanges manufacturer in India, check temperature range & coating of Werkstoff P235GH TC1 weld neck flanges

P235GH EN 10217-2 forged flanges temperature range

  • 200 °C to maximum 400 °C

P235GH TC1 blind flanges coating

Antirust light oil

Antirust light oil

Black paint coating

Black paint coating

Yellow paint coating

Yellow paint coating

 

Manufacturing Origin and Standards

Australia and UK Italy Europe Europe USA
BS 10 UNI 2276/ 6091 BS EN 1092-1 (Steel) BS EN 1092-3 (Alloy) ANSI
Germany China Russia Japan Europe France
DIN GB/T 9112 / 9119 Ghost JIS ISO 7005, BS EN 1092-2 (Iron), PN NF E 29-200/ NF E 29-203
Canada Europe USA Korea Malaysia Australia
CSA B16.5/ B16.47 EN ASME, ASTM, MSS SP44, AWWA, API-605 KS MS 816, MS 253 AS 2129

 

View P235GH chemical composition, hardness, and density of steel Grade P235GH slip on flanges

P235GH chemical composition

Element Composition %
Carbon ≤0.16
Niobium ≤0.020
Nickel ≤0.30
Silicon ≤0.35
Manganese 0.60 to 1.20
Phosphorus 0.025
Copper ≤0.30
Chromium ≤0.30
Aluminium ≤0.020
Titanium 0.03
Hexavalent chromium compounds (Vi) ≤0.02
Nitrogen ≤0.012
Molybdenum ≤0.08
Sulfur 0.015

 

Hardness of pressure vessel P235GH steel pipe flanges

  • Brinell Hardness = 120

Density for Carbon steel P235GH hot forged flange

Property Unit Value
Density g/cm³ 7.85

 

Learn about the pressure vessel P235GH steel pipe flanges mechanical requirements and carbon steel P235GH hot forged flange heat treatment

P235GH (1.0345) flange mechanical requirements

Nominal Thickness In MM Tensile strength (MPa) (+N)
to 100 360-480
100 – 150 350-480
150 – 250 340-480

 

Nominal Thickness In MM (Min.) Yield Strength (MPa) (+N)
to 16 235
16 – 40 225
40 – 60 215
60 – 100 200
100 – 150 185
150 – 250 170

 

P235GH allowable stress

  • 9.9 KSI
  • Limited to 500 deg F

 

P235GH TC2 steel flange heat treatment

Heat Solution
N+T Normalizing + Tempering
Q+T Quenching + Tempering

 

Heat Treatment Temperature
Hot working temperature 1100~850 ℃
Annealing temperature 890~950 ℃
Normalizing temperature 520~580 ℃

 

 

P235gh Material equivalent

EN (P235GH)
USA A285
Germany (DIN & WNr) 1.0345
Japan (JIS) SB410/ SGV410/ SPV235
France (AFNOR) A37AP/ A37CP
England (BS) 141-360
Italy (UNI) Fe360-1KG/ Fe360-1KW
Belgium (NBN) D37-1.2/ E37-1.2
Spain (UNE) A37RCI
China (GB) 20
Sweden (SS) 1330/ 1330-01
Poland (PN) St36K
Austria (ONORM) St35KW
Russia (GOST) 12k
India (IS) Grade 1